2014 Aluminium Sheets Manufacturer
Corrosion Resistance and Protective Measures
While the 2014 alloy offers remarkable strength, its corrosion resistance is relatively low compared to other aluminium alloys. To mitigate this, several protective measures are recommended:

Why Choose 1100 Aluminium Sheets?
1100 aluminium sheet is primarily known for its exceptional resistance to corrosion and high formability. It’s an ideal choice for applications where these attributes are required, such as manufacturing and industrial uses. Whether you need aluminium sheet grade 1100 for creating durable equipment or for roofing solutions, this alloy offers superior protection against weather elements, UV radiation, and environmental corrosion.
Related
Products
Key Properties of 2014 Aluminium Sheets
- High Strength: The alloy’s primary advantage is its superior strength, making it ideal for structural applications.
- Excellent Machinability: 2014 aluminium sheets are known for their ease of machining, allowing for precise manufacturing processes.
- Thermal and Electrical Conductivity: While not as high as pure aluminium, the alloy maintains decent conductivity, suitable for specific applications.
- Density: Approximately 2.80 g/cm³, balancing strength with weight.

Applications of 2014 Aluminium Sheets
Due to their unique properties, 2014 aluminium sheets are extensively used in:
- Aerospace Industry: Ideal for aircraft structures and components requiring high strength-to-weight ratios.
- Automotive Sector: Used in high-performance vehicles for parts like chassis and suspension components.
- Military Applications: Suitable for armored vehicles and other defense equipment.
- Machinery and Equipment: Employed in manufacturing equipment where durability and precision are crucial.
Chemical Composition Of 2014 Aluminium Sheets & Plates
Chemical Element | % Present |
---|---|
Silicon (Si) | 0.50 – 0.90 |
Iron (Fe) | 0.0 – 0.50 |
Copper (Cu) | 3.90 – 5.00 |
Zinc (Zn) | 0.0 – 0.25 |
Manganese (Mn) | 0.40 – 1.20 |
Magnesium (Mg) | 0.20 – 0.80 |
Titanium (Ti) | 0.0 – 0.15 |
Others (Total) | 0.0 – 0.15 |
Chromium (Cr) | 0.0 – 0.10 |
Nickel (Ni) | 0.0 – 0.10 |
Other (Each) | 0.0 – 0.05 |
Titanium + Zirconium (Ti+Zr) | 0.0 – 0.20 |
Aluminium (Al) | Balance |
Mechanical Properties Of 2014 Aluminium Sheets & Plates
Mechanical Property | Value |
---|---|
Tensile Strength | 440 Min MPa |
Proof Stress | 390 Min MPa |
Hardness Brinell | 133 HB |
Physical Properties Of 2014 Aluminium Sheets & Plates
Physical Property | Value |
---|---|
Density | 2.82 g/cm³ |
Modulus of Elasticity | 71 GPa |
Electrical Resistivity | 0.045 x10^-6 Ω .m |
Thermal Conductivity | 138 W/m.K |
Thermal Expansion | 23 x10^-6 /K |
Melting Point | 535 °C |
Metalco Extrusions Global LLP: Your Trusted Partner
As a premier 2014 aluminium sheet manufacturer, Metalco Extrusions Global LLP is committed to delivering products that meet stringent quality standards. Our state-of-the-art manufacturing facility in Bangalore ensures that each sheet undergoes rigorous testing and quality checks.
Why Choose Us?
- Quality Assurance: Adherence to international standards ensures top-notch products.
- Customization: Tailored solutions to meet specific client requirements.
- Competitive Pricing: Transparent and competitive 2014 aluminium sheet price structures.
- Timely Delivery: Efficient logistics ensure prompt delivery, minimizing downtime.
Technical Specifications and Standards
Our 2014 aluminium sheets conform to various international standards, including:
- ASTM B209: Standard Specification for Aluminium and Aluminium-Alloy Sheet and Plate.
- EN 485-2: Aluminium and aluminium alloys. Sheet, strip, and plate. Mechanical properties.
Mechanical Properties
The mechanical properties of our 2014 aluminium sheets are as follows:
Tensile Strength: Ranges from 190 to 480 MPa, depending on the temper.
Yield Strength: Typically around 400 MPa.
Elongation at Break: Approximately 10-15%, indicating good ductility.
Heat Treatment and Processing
The 2014 alloy responds well to heat treatment, enhancing its mechanical properties. Common tempers include:
T3: Solution heat-treated and cold worked.
T4: Solution heat-treated and naturally aged.
T6: Solution heat-treated and artificially aged.
Each temper offers a unique balance of strength and ductility, allowing for versatility in application.
Fabrication and Welding
While 2014 aluminium sheets exhibit excellent machinability, welding can be challenging due to the alloy’s susceptibility to cracking. Specialized